PA66 GF30 is a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness, high-temperature resistance and easy forming.
The mechanical strength, creep resistance and fatigue strength of 30% reinforced Nylon66 are greatly improved, and the elongation, mold shrinkage, moisture absorption, and wear resistance are reduced. It can be injection-molded plastic parts with stressed structures in the fields of automobiles, E & E, home appliances and machinery industries.
Physical Property
Ash | (30.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1365Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.2-0.5 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.6-0.9% I ISO294-4) |
Mechanical Properties
Tensile strength (186.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.4% I ISO527) Conditioned | 5mm/min |
Notched Impact Strength (12.5 KJ/m2 IISO179) Conditioned | 1.0J |
Flexural Strength (282MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (8518 MPa I ISO178) Conditioned | 2mm/ min |
Thermal Property
Melting Point | (260°C I ISO11357) |
Hot Deformation Temperature | (250*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 280-300°C |
Nozzle Temperature | 280-300*C |
Tooling Temperature | 80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！