PA 6 GF30 is a 30 % glass fiber reinforced polyamide.
The mechanical properties, dimensional stability, heat resistance, and aging resistance of PA are significantly improved, and the fatigue strength is 2.5 times that of enhancement when 30% glass fiber is added to PA. At the same time, PA6 GF30 is the most widely used product in various industries. Engineering plastic products can meet the requirements of industry and daily usage.
Enhanced grade PA6 gf30 is workable for high-strength, high-wear-resistant structural parts, mainly used in machinery, vehicles, electronic and electrical, textiles, and sports equipment.
Such as the exterior mirror and door handle of the automobile as well as the engine cover.
Physical Property
Ash | (15.0% 1 ISO3451/1) |
Conditioned | 600°C*2h |
Density | (1250Kg/m3 1 ISO1183) |
Conditioned | 23°C |
Shrinkage Parallel Flow | (0.5-0.7 % 1 ISO294-4) |
Shrinkage Vertical Flow | (0.7-1.1% I ISO294-4) |
Mechanical Properties
Tensile strength (125.0MPa 1 ISO527) Conditioned | 5mm/ min |
Tensile Strain at Break (2.5% I ISO527) Conditioned | 1.0J |
Notched Impact Strength (125 0MPa I ISO527) Conditioned | 2mm/min |
Flexural Strength (190MPa 1ISO178) Conditioned | 2mm/min |
Flexural Modulus (5700 MPa I ISO178) Conditioned | 5mm/ min |
Thermal Property
Melting Point | (220°C I ISO11357) |
Hot Deformation Temperature | (175*C I ISO75) |
Conditioned | 1.8MPa |
Flammability Class | (HB 1UL94) |
Conditioned | mm |
Injection Molding Conditions
Drying Temperature | 130°C |
Drying Time | 3h |
Cylinder Temperature | 240-260°C |
Nozzle Temperature | 240-260*C |
Tooling Temperature | 80*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！